Effect of Europium Substitution on the Structural and Magnetic Properties of Nanocrystalline Cobalt Ferrite
A series of Europium-substituted cobalt ferrites (CoEuxFe2-xO4 with = 0.00, 0.10, 0.20, 0.30) were synthesized by hydrothermal method. The structural characterizations of all the prepared samples were done using XRD and FTIR. These studies confirmed the formation of single-phase spinel structure in all the compositions. The increase in the value of lattice parameter with increase in Europium concentration suggests the ... إقراء المزيد

2018-11-17 06:02:37 الكلمات المفتاحية Doping, TEM, SEM, XRD, superparamagnetic materials, Ferrites, VSM,
Doping of Nano Zinc  Ferrites by Chromium: Structural and Magnetic Properties Studies
A SERIES OF CHROMIUM-SUBSTITUTED ZINC FERRITES (CRXZN FE2-XO4 WITH = 0.00, 0.10, 0.20, 0.30, 0.40) WERE SYNTHESIZED VIA HYDROTHERMAL METHOD. THE STRUCTURAL CHARACTERIZATIONS OF ALL THE PREPARED SAMPLES WERE DONE USING XRD, FTIR AND EDAX, TEM, HR-TEM AND TGA MEASUREMENTS . THESE STUDIES CONFIRMED THE FORMATION OF SINGLE-PHASE INVERSE SPINEL STRUCTURE IN ALL THE COMPOSITIONS. FROM HR-TEM MEASURMENTS, CRYSTALLINITY ARE ... إقراء المزيد

2018-10-05 12:09:59 الكلمات المفتاحية EDAX, XRD, particle size, Magnetic properties, structural, Cobalt Ferrites, Doping, TEM, SEM, FT-IR,
Doping of Nano Cobalt Ferrites by Cupper: Structural and Magnetic Properties Studies
A series of Cupper-substituted cobalt nano ferrites (CuxCo1-x Fe2O4 with = 0.00, 0.10, 0.20, 0.30 and 0.4) was synthesized via hydrothermal method. The structural characterizations of all the prepared nanoparticles were performed using powder x-ray diffraction, EDAX and FTIR analyses. These studies confirmed the formation of single-phase spinel structure in at lower compositions. The increase in the value of lattice ... إقراء المزيد