Duplex treatment of 304 AISI stainless steel using rf plasma nitriding and carbonitriding

2018-09-26 12:09:21 الكلمات المفتاحية Surface morphology, Microstructure, Surface hardness, Glow discharge optical spectro, Carbonitriding, Duplex treatment,
Duplex treatment of 304 AISI stainless steel using rf plasma nitriding and carbonitriding
Surface of 304 AISI austenitic stainless steel has been modified using duplex treatment technique of nitriding and carbonitriding. A thick modified nitrided layer, of approximately 20 μm, has been achieved when rf inductively coupled plasma was adjusted at 450 W for processing time of only 10 min. After performing the nitrided layer, the nitrided samples were carbonitrided using the same ... إقراء المزيد

Duplex treatment of AISI 304 austenitic stainless steel using rf nitriding and dc reactive magnetron sputtering of titanium

2018-09-26 12:14:25 الكلمات المفتاحية Duplex treatment, Titanium nitride, Glow discharge optical spectro, Microstructure, Surface hardness,
Duplex treatment of AISI 304 austenitic stainless steel using rf nitriding and dc reactive magnetron sputtering of titanium
In this work, duplex treatment has been carried out using radio frequency (rf) plasma nitriding process and direct current (dc) magnetron sputtering of titanium. Nitriding of AISI 304 stainless steel, using rf plasma technique, created a thick modified layer of approximately 20 μm for short plasma processing time of 10 min. After nitriding process, a thin titanium nitride film has ... إقراء المزيد

  • «